Specification
XS-FR-C301 is a nitrogen, phosphorus composite flame retardant, mainly used for fabric coating, After the coating glue is added to this product when it comes in contact with the flame, the surface will form a carbon layer that expands several times and is dense, heat insulation, oxygen and flammable gas, which can effectively prevent the decomposition of organic fabrics and contact with oxygen.
Under suitable formula and process conditions, it can meet the requirements of BS5852, NFPA701 and other fabric flame retardant standards.
Characteristics | Unit | Value |
Appearance | / | White Powder |
Phosphorus Content | 0 | 22~27 |
Water Content | 0 | ≤0.5 |
Nitrogen Content | g/cm³ | 15~20 |
Bulk Density | g/cm³ | ~0.8 |
Average Particle Size (D50) | um | 10~20 |
XS- FR-C301 is suitable for flame retardant of solvent-based acrylic pressure-sensitive adhesive, polyurethane rubber, and adhesive. To prepare flame retardant tapes and various coating adhesives on flexible substrates, the recommended dosage s 35%~40%.
Manufacturing Facility in XUSEN
Professional Composite Flame Retardant For Fabric Coating XS- FR-C301 manufacturer in China, We currently achieved an annual production capacity of 12,000 tons. We can also OEM, simply wholesale Composite Flame Retardant For Fabric Coating XS- FR-C301 direct from manufacturer. We have our own production workshops and warehouses, equipped with complete production and quality inspection equipment.
Composite flame retardants can be effectively used with various types of polyester, but the compatibility and performance can vary based on several factors:Types of Polyester:Polyethylene Terephthalat...
READ MOREFunctional additive masterbatches play several critical roles in plastic processing by enhancing the properties and performance of polymer materials. Here’s a detailed look at their functions:Property...
READ MOREComposite flame retardants are designed not only to provide fire resistance but also to maintain key mechanical properties, such as tensile strength and flexibility, after incorporation into materials...
READ MORE